UHP 500 mm dia. 20 inch ovengrafietelektrode met tepels
Technische parameter
Fysische en chemische eigenschappen voor D500mm (20”) elektrode en tepel
| Parameter | Deel | Eenheid | UHP 500 mm (20”) gegevens |
| Nominale diameter | Elektrode | mm(inch) | 500 |
| Maximale diameter | mm | 511 | |
| Minimale diameter | mm | 505 | |
| Nominale lengte | mm | 1800/2400 | |
| Maximale lengte | mm | 1900/2500 | |
| Minimale lengte | mm | 1700/2300 | |
| Maximale stroomdichtheid | KA/cm2 | 18-27 | |
| Huidige draagkracht | A | 38000-55000 | |
| Specifieke weerstand | Elektrode | μΩm | 4,5-5,6 |
| Nippel | 3,4-3,8 | ||
| Buigsterkte | Elektrode | Mpa | ≥12,0 |
| Nippel | ≥22,0 | ||
| Young-modulus | Elektrode | Gpa | ≤13,0 |
| Nippel | ≤18,0 | ||
| Bulkdichtheid | Elektrode | g/cm3 | 1,68-1,72 |
| Nippel | 1,78-1,84 | ||
| CTE | Elektrode | ×10-6/℃ | ≤1,2 |
| Nippel | ≤1,0 | ||
| Asinhoud | Elektrode | % | ≤0,2 |
| Nippel | ≤0,2 |
OPMERKING:Elke specifieke vereiste inzake afmetingen kan worden aangeboden.
Toepassingen
- Elektrische boogoven
Grafietelektroden worden voornamelijk gebruikt in het moderne staalproductieproces. Electric Arc Furnace wordt algemeen erkend als een van de meest efficiënte en betrouwbare gereedschappen. Een vlamboogoven gebruikt grafietelektroden om hoge temperaturen te creëren en stroom op te wekken, die vervolgens wordt gebruikt om gerecycled staalschroot te smelten. Omdat de diameter van de grafietelektrode een cruciale rol speelt bij het creëren van het noodzakelijke warmteniveau en het garanderen van een eindproduct van hoge kwaliteit, is het gebruik van de juiste elektrode cruciaal voor het bereiken van optimale resultaten. Afhankelijk van de capaciteit van de elektrische oven, zijn grafietelektroden met verschillende diameters uitgerust om ervoor te zorgen dat de grafietelektroden nog steeds worden gebruikt, de grafietelektroden zijn verbonden door nippels. - Ondergedompelde elektrische oven
De ondergedompelde elektrische oven is een revolutionair product dat is ontworpen om aan de behoeften van de moderne industrie te voldoen. Deze ultramoderne oven is voorzien van een UHP-grafietelektrode die speciaal is vervaardigd om de efficiëntie van het smeltproces te verbeteren. De grafietelektrode in de ondergedompelde elektrische oven wordt voornamelijk gebruikt voor de productie van ferrolegeringen, puur silicium, gele fosfor, mat en calciumcarbide. Het unieke ontwerp van deze elektrische oven onderscheidt hem van traditionele ovens, omdat een deel van de geleidende elektrode in de oplaadmaterialen kan worden begraven. - Weerstandsoven
Weerstandsovens worden gebruikt om hoogwaardige grafietproducten te produceren, zoals UHP-grafietelektroden. Deze elektroden worden veel gebruikt in het staalproductieproces met elektrische boogovens om hoogwaardig staal te produceren. De UHP-grafietelektrode staat bekend om zijn hoge thermische geleidbaarheid, lage elektrische weerstand en weerstand tegen thermische schokken. Deze eigenschappen maken ze tot een ideale keuze voor het staalproductieproces. UHP-grafietelektroden worden geproduceerd door een grafitiseringsproces bij hoge temperatuur in een weerstandsoven.
Gufan Cabon conische tepel- en sockettekening
Gufan Carbon conische nippel en socketafmetingen (4TPI)
| Gufan Carbon conische nippel en socketafmetingen (4TPI) | |||||||||
| Nominale diameter | IEC-code | Maten van tepels (mm) | Maten van stopcontact (mm) | Draad | |||||
| mm | inch | D | L | d2 | I | d1 | H | mm | |
| Tolerantie (-0,5~0) | Tolerantie (-1~0) | Tolerantie (-5~0) | Tolerantie (0~0,5) | Tolerantie (0~7) | |||||
| 200 | 8 | 122T4N | 122.24 | 177,80 | 80.00 uur | <7 | 115,92 | 94,90 | 6.35 |
| 250 | 10 | 152T4N | 152,40 | 190,50 | 108.00 uur | 146.08 | 101.30 uur | ||
| 300 | 12 | 177T4N | 177,80 | 215,90 | 129.20 | 171,48 | 114.00 uur | ||
| 350 | 14 | 203T4N | 203.20 | 254,00 | 148,20 | 196,88 | 133,00 | ||
| 400 | 16 | 222T4N | 222.25 | 304,80 | 158,80 | 215,93 | 158,40 | ||
| 400 | 16 | 222T4L | 222.25 | 355,60 | 150,00 | 215,93 | 183,80 | ||
| 450 | 18 | 241T4N | 241.30 | 304,80 | 177,90 | 234,98 | 158,40 | ||
| 450 | 18 | 241T4L | 241.30 | 355,60 | 169,42 | 234,98 | 183,80 | ||
| 500 | 20 | 269T4N | 269,88 | 355,60 | 198,00 | 263,56 | 183,80 | ||
| 500 | 20 | 269T4L | 269,88 | 457,20 | 181.08 | 263,56 | 234,60 | ||
| 550 | 22 | 298T4N | 298,45 | 355,60 | 226,58 | 292.13 | 183,80 | ||
| 550 | 22 | 298T4L | 298,45 | 457,20 | 209,65 | 292.13 | 234,60 | ||
| 600 | 24 | 317T4N | 317,50 | 355,60 | 245,63 | 311.18 | 183,80 | ||
| 600 | 24 | 317T4L | 317,50 | 457,20 | 228,70 | 311.18 | 234,60 | ||
Gerelateerde producten
-
Grafietelektroden Tepels 3tpi 4tpi-aansluit...
Beschrijving De grafietelektrodenippel is een klein maar essentieel onderdeel van het EAF-staalproductieproces. Het is een cilindervormig onderdeel dat de elektrode met de oven verbindt. Tijdens het staalproductieproces wordt de elektrode in de oven neergelaten en in contact gebracht met het gesmolten metaal. Elektrische stroom vloeit door de elektrode en genereert warmte, waardoor het metaal in de oven smelt. De tepel speelt een cruciale rol bij het onderhoud...
-
Koolstofblokken Geëxtrudeerde grafietblokken EDM-iso...
Technische parameter Fysische en chemische indexen voor grafietblok Artikel Eenheid GSK TSK PSK Korrel mm 0,8 2,0 4,0 Dichtheid g/cm3 ≥1,74 ≥1,72 ≥1,72 Weerstand μ Ω.m ≤7,5 ≤8 ≤8,5 Druksterkte Mpa ≥36 ≥35 ≥34 As% ≤0,3 ≤0,3 ≤0,3 Elasticiteitsmodulus Gpa ≤8 ≤7 ≤6 CTE 10-6/℃ ≤3 ≤2,5 ≤2 Buigsterkte Mpa 15 14,5 14 Porositeit % ≥...
-
Koolstofadditief Carbon Raiser voor staalgieten...
Gecalcineerde petroleumcokes (CPC) Samenstelling Vaste koolstof (FC) Vluchtige stoffen (VM) Zwavel As Vocht ≥96% ≤1% 0≤0,5% ≤0,5% ≤0,5% Grootte: 0-1 mm, 1-3 mm, 1 -5 mm of naar keuze van de klant Verpakking: 1. Waterdichte PP geweven zakken, 25 kg per papier zak, 50 kg per kleine zak 2.800 kg - 1000 kg per zak als waterdichte jumbozakken Hoe gecalcineerde petroleumcokes (CPC) te produceren Pijn ...
-
Oven Grafietelektrode Regelmatig vermogen RP Gr...
Technische parameter Parameter Onderdeel Eenheid RP 550 mm (22”) Gegevens Nominale diameter Elektrode mm (inch) 550 Max. diameter mm 562 Min. diameter mm 556 Nominale lengte mm 1800/2400 Max. lengte mm 1900/2500 Min. lengte mm 1700/2300 Max. stroomdichtheid KA /cm2 12-15 Stroombelastbaarheid A 28000-36000 Specifieke weerstand Elektrode μΩm 7,5-8,5 Nippel 5,8-6,5 Buig...
-
UHP 400 mm Turkije grafietelektrode voor EAF LF...
Technische parameter Parameter Onderdeel Eenheid UHP 400 mm (16”) Gegevens Nominale diameter Elektrode mm (inch) 400 (16) Max. diameter mm 409 Min. diameter mm 403 Nominale lengte mm 1600/1800 Max. lengte mm 1700/1900 Min. lengte mm 1500/1700 Max. Stroomdichtheid KA/cm2 16-24 Stroombelastbaarheid A 25000-40000 Specifieke weerstandselektrode μΩm 4,8-5,8 Nippel 3,4-4,0 F...
-
Hoogvermogen grafietelektrode voor EAF LF-smelterij
Technische parameter Parameter Onderdeel Eenheid HP 350 mm (14”) Gegevens Nominale diameter Elektrode mm (inch) 350 (14) Max. diameter mm 358 Min. diameter mm 352 Nominale lengte mm 1600/1800 Max. lengte mm 1700/1900 Min. lengte mm 1500/1700 Huidig Dichtheid KA/cm2 17-24 Stroombelastbaarheid A 17400-24000 Specifieke weerstandselektrode μΩm 5,2-6,5 Nippel 3,5-4,5 Buig...